White PETG Plastic Sheet Environmental Protection Material For ID Card Produciton
Product Details:
Place of Origin: | China |
Brand Name: | MKarte |
Model Number: | MCS-PETG |
Payment & Shipping Terms:
Minimum Order Quantity: | 30000 sheets or 2 tons |
---|---|
Price: | Negotiable |
Packaging Details: | 50 or 100 or 200 sheets per bag, 10 bags per paper carton, and the cartons are piled up and firmly fixed on solid plywood pallets |
Delivery Time: | 10-15 work days |
Payment Terms: | T/T, L/C, D/A, Western Union, MoneyGram |
Supply Ability: | 50000 Sheets per Week |
Detail Information |
|||
Material: | PETG,Polyethylene Terephthalate | Color: | White Or Customized |
---|---|---|---|
Vicat: | 78-80 ± 2 | Density ( G/cm3): | 1.30 ±0.05 |
Thickness Range: | 0.10-0.76 | Laminating Temp: | 120 Degrees Celcius |
High Light: | petg clear plastic sheet,clear petg sheet |
Product Description
White PETG core sheet / PETG Card Base environmental protection material for ID card produciton
1.White PETG core sheet / PETG Card Base environmental protection material - Introduction
White PETG core sheet / PETG Card Base is widely used in card base production. It has such features as impact resistance, high temperature resistance, anti-static, abrasion, folding and high strength. It is widely used for the production of high-end credit cards, ID cards and passport, etc.
PETG is a kind of transparent amorphous copolyester.
Features:
1).Excellent strength and wear-resisting
2).High temperature and low temperate resistance;
3).Perfect application for laser Engraving
4).Environment-friendly material
5).Longer service life
Item | PETG Core Sheet |
Color | White |
Thickness Range(mm) | 0.1-0.76 |
Vicat point ℃ | 78-80 ± 2 |
Tensile strength | ≥50 Mpa |
Surface | Both sides matt |
Density | 1.3 ± 0.05 |
Transparency | ≤5 |
Heat shrink | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
2.White PETG core sheet / PETG Card Base - Parameters
It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection.
Technical Parameters:
Item | Parameters |
Vicat softening point (B50) | 78±2 |
Vicat softening point (A120) | 80±2 |
Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
Surface Dyne (dynes/cm) | ≥38 |
Normal thickness in mm | 0.10-0.76 |
Density (g/cm3) | 1.30 ±0.05 |
Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
Aging time (65℃ temp./95% humidity ) | >200 hours |
Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
3.White PETG core sheet / PETG Card Base- Application
Card-making method:
1). Print the patterns directly to the material
2). Laminate with overlay
3). Punching
4). Other art-work
Product model | Product name | Thickness Range mm | Color | Vicat ℃ | dynes/cm | Apparent density g/cm3 | Peel strength N/cm | Main application |
PETG | PETG core | 0.1-0.76 | White | 78-80 | ≥38 | 1.3+/-0.05 | / | It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection. |
Detailed Product Description
1.Thickness:0.1mm to 0.76mm
2.Color: White or customized
3.Surface tension: ≥38 dynes/cm
Characteristic
1.Good lamination properties
2.Good impact resistance
3.Good chemical resistance
4.Excellent printability with either offset or screen printing
5.Laminating Temp 120 degrees Celcius-130 degrees Celcius (lab conditions)