Transparent Uncoated Overlay PC Plastic Sheet For Normal PC Card Production
Product Details:
| Place of Origin: | China |
| Brand Name: | MKarte |
| Model Number: | MUO-PC |
Payment & Shipping Terms:
| Minimum Order Quantity: | 20000 sheets |
|---|---|
| Price: | negotiated |
| Packaging Details: | in reel or 500 sheets per bag/4 bags per paper carton, or as per customer requirements |
| Delivery Time: | 10-15 working days |
| Payment Terms: | D/P, L/C, , T/T, Western Union, MoneyGram |
| Supply Ability: | 50000 Sheet/Sheets per Week |
|
Detail Information |
|||
| Size: | In Sheet Or Reel, Size As Per Customer Requirements | Normal Thickness In Mm: | 0.04-0.10 |
|---|---|---|---|
| Color: | Transparent Without Coating On Surface. | Package Method: | In Reel Or 500 Sheets Per Bag/4 Bags Per Paper Carton, Or As Per Customer Requirements |
| Storage Condition: | Sealed, Moisture-proof, Room Temperature Under 40℃, Keep It Horizontally, Avoid Heavy Pressing And Direct Sunlight. | Laser Engraving Performance: | Cannot Be Laser Engraved. |
| Highlight: | clear polycarbonate sheet,polycarbonate transparent sheet |
||
Product Description
Polycarbonate ( PC ) Card uncoated Overlay for Normal PC Card Production
Polycarbonate (PC) Card uncoated Overlay (Model: MUO-PC) is specially produced for PC card body lamination with printed sheets. It has such good features like strong lamination adhesion, excellent tensile strength, wear resistance and high temperature resistance. It is widely used in such cards as anti-fake IC cards, driving license card, transportation card and passport etc.
1.Polycarbonate ( PC ) Card uncoated Overlay - Introduction
Brief Introduction:
Polycarbonate (PC) Card uncoated Overlay is a new developed environment friendly product which could get excellent peel strength at high temperature. It provides superior aging resistance performance to other similar products, no color change and deformation after lamination.
Characteristics:
● Work well at high temperature,no color change with fluorescent ink.
● Abrasion resistant , prolong the life of cards.
● Environment friendly, no solvent or gas discharged.
| Item | Specification | Test Method |
| Thickness | 40-100um | |
| Thickness tolerance |
＞0.5±6um ≤0.5±4um |
|
| Density | 1.2±0.05 g/cm3 | ASTM D792 |
| Surface tension(front) | ≥38Dynes/cm | ASTM D1922 |
| Surface tension(back) | ≥38Dynes/cm | ASTM D1922 |
| Shrinkage | ＜1.0 | ASTM D1204 |
| Vicat | 147±20C | ASTM D1525 |
| Tensile strength | ≥50 N/mm2 | ASTM D1922 |
| Surface roughness | 0.5um-1.8um |
2.Polycarbonate ( PC ) Card uncoated Overlay - Parameters
1). Size: in sheet or reel, A4, A3 or as per customer requirements
2). Normal thickness in mm: 0.04,0.05,0.06,0.08,0.10
3). Color: transparent without coating on surface.
4). Package method: in reel or 500 sheets per bag/4 bags per paper carton, or as per customer requirements.
5). Storage condition: Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight.
6). Laser engraving performance: cannot be laser engraved.
| Item | Unit | Value | |
| Density | g/cm3 | 1.20 ±0.05 | |
| Tensile Strength | Horizontal | MPa | ≥50 |
| Vertical | ≥50 | ||
| Vicat | ℃ | 147±2 | |
| Surface Dyne | dynes/cm | ≥38 | |
3.Polycarbonate ( PC ) Card uncoated Overlay - Application
Application :
such as identity card,driving card, passport etc.
| Item | Parameters | |
| Vicat (℃) | 147±2 | |
| Shrinkage | MD/TD | ＜1.0 |
| Tensile Strength (MPa) | MD | ≥50 |
| TD | ≥50 | |
| Roughness(μm) | Ra | 0.58, 1.5-2.1 |
| Ra | 3.45 | |
| Thickness(mm) | 0.04-0.1 | |
◆Laminating Condition:
| Laminating Unit | Temp(℃) | Pressure(MPa) | Time (min) |
| Heat Laminating | 140~155 | ≥6 | 25 |
| Cool Laminating | ≤25 | ≥6 | 15 |
4.Polycarbonate ( PC ) Card uncoated Overlay - Packing
◆Packing:
Outer:Carton Inner:PE bag
◆Storage:
Keep package sealed and moisture-proof, room temperature under 40℃
Keep horizontally, avoid oppress heavily and direct sun light.
Stacking height should not exceed one meter.
Shelf life: Two year.
Storage conditions:
Ideal storage conditions between 10-30 0C, Ideal RH 40%. Should not be stored in direct sunlight and avoid major thermal fluctuation, store in original packing. Film should be conditioned a minimum of 24 hours at ambient room temperature.
Recommended use of material within one year of production date.