0.50mm Polycarbonate A3 Plastic Film Overlay For PC Card Body Laminaiton
Product Details:
| Place of Origin: | China |
| Brand Name: | MK |
| Model Number: | MCO-PC |
Payment & Shipping Terms:
| Minimum Order Quantity: | 30000 sheets |
|---|---|
| Price: | Negotiatable |
| Packaging Details: | By reel or 500 sheets per bag/4 bags per paper carton, or as per customer requirements |
| Delivery Time: | 10-15 working days |
| Payment Terms: | D/P, L/C, , T/T, Western Union, MoneyGram |
| Supply Ability: | 50000 Sheets per Week |
|
Detail Information |
|||
| Normal Thickness In Mm: | 0.05/0.075/0.125/0.175/0.25/0.375/0.50mm Etc | Color: | Semi-transparent And High Haze |
|---|---|---|---|
| Future: | Moisture Proof | Surface: | Matt/Matt, Flat, No Defect, No Dust. |
| Coating Availability: | With Or Without Coating Are Both Ok. | Packing: | PE Film Inside + Carton Box+Pallet |
| High Light: | A3 Plastic Film Overlay,A3 Polycarbonate Film Overlay,0.50mm Plastic Film Overlay |
||
Product Description
A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
Polycarbonate has many special characteristics that other engineering plastics don’t contain, due to the flexible carbonate group and the rigid benzene ring in its molecular structure. Therefore it’s widely used. Due to the specialty in its structure, PC has a range of unique advaes such as excellent light transmittance, relatively high glass transition temperature, desirable chemical modification, easy for physical modification, excellent impact toughness, creep resistance, electrical in insulation and weathering resistance.
PC films and sheets that made from polycarbonate have a wide range of temperature (-30~120℃), dimensional stability, excellent comprehensive properties and easy to process, therefore they are very widely used.
1. Introduction of A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton is specially produced for PC card body lamination with printed sheets. It has such good features like strong lamination adhesion, excellent tensile strength, wear resistance and high temperature resistance. It is widely used in such cards as anti-fake IC cards, driving license card, transportation card and passport etc.
● Work well at high temperature,no color change with fluorescent ink.
● Abrasion resistant , prolong the life of cards.
● Environment friendly, no solvent or gas discharged.
| Item | Specification | Test Method | |
| Thickness | 40-100um | ||
| Thickness tolerance |
＞0.5±6um ≤0.5±4um |
||
| Density | 1.2±0.05 g/cm3 | ASTM D792 | |
| Surface tension(front) | ≥34Dynes/cm | ASTM D1922 | |
| Surface tension(back) | ≥34Dynes/cm | ASTM D1922 | |
|
Heating Shrinkage (%) (135℃±2,10min) |
Thickness≤ 0.175mm | MD | ≦2.5 |
| CD | ≦0.5 | ||
| Vicat | 147±20C | ASTM D1525 | |
| Tensile strength | ≥50 N/mm2 | ISO527-3 | |
| Surface roughness | 0.5um-1.8um | ||
2.Specification of A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
1). Size: in sheet or reel, A4, A3 or as per customer requirements
2). Normal thickness in mm: 0.04,0.05,0.06,0.08,0.10
3). Color: transparent, with/without coating on surface are both ok.
4). Package method: in reel or 500 sheets per bag/4 bags per paper carton, or as per customer requirements.
5). Storage condition: Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight.
6). Laser engraving performance: can be laser engraved.
| Technical parameters | |||
| Item | Standard Value | ||
|
Thickness (mm) |
0.04-0.1 ( ±5%) | ||
| Surface | Matt/Matt, flat, no defect, no dust. | ||
| Tensile Strength (Mpa) -ISO527-3 | ≧50(MD/CD) | ||
| Break Strength (%) -ISO527-3 | ≧60(MD/CD) | ||
|
Folding Capacity
|
Thickness <0.25mm, ≧13 | ||
| Thickness ≧0.25mm,≧11 | |||
| Light Transmittance (%) | ≧80 | ||
| Haze (%) | ≦ 90 | ||
| Surface Tension(Dynes/cm) -ISO 8296-2003 | ≧34 | ||
|
Heating Shrinkage (%) (135℃±2,10min) |
Thickness≤ 0.175mm | MD | ≦2.5 |
| CD | ≦0.5 | ||
| Vicat Softening Temperature(℃) - ISO 306-1994 | 150±3 | ||
| Coating availability | with coating or w/o coating are both OK. | ||
3.Application of A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
| Item | Parameters | |
| Vicat (℃) | 147±2 | |
| Shrinkage | MD/TD | ＜1.0 |
| Tensile Strength (MPa) | MD | ≥50 |
| TD | ≥50 | |
| Roughness(μm) | Ra | 0.58, 1.5-2.1 |
| Ra | 3.45 | |
| Thickness(mm) | 0.04-0.1 | |
◆Laminating Condition:
| Laminating Unit | Temp(℃) | Pressure(MPa) | Time (min) |
| Heat Laminating | 140~155 | ≥6 | 25 |
| Cool Laminating | ≤25 | ≥6 | 15 |
4. Packing of A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
Outer:Carton Inner:PE bag
5.Storage of A3 Size Polycarbonate Plastic Sheet Overlay Film Suitable For PC Card Body Laminaiton
Storage:
Keep package sealed and moisture-proof, room temperature under 40℃
Keep horizontally, avoid oppress heavily and direct sun light.
Stacking height should not exceed one meter.
Shelf life: Two years.
Storage conditions:
Ideal storage conditions under 40℃ of room temperature, Ideal RH 40%. Should not be stored in direct sunlight and avoid major thermal fluctuation, store in original packing. Film should be conditioned a minimum of 24 hours at ambient room temperature.
Recommended use of material within one year of production date.
Long-term performance
Polycarbonate films also offer excellent mechanical and thermal properties. They are resistant to heat up to 145°C and do not warp after extended exposure to high temperatures. Polycarbonate retains its stiffness even at low temperatures.
Polycarbonate is used to make CDs, bulletproof glass, water bottles and, increasingly, cards and secure passport laminates. Stronger and more expensive than PVC, its durability makes polycarbonate an ideal material for cards intended for a service life of ten years or more, such as national ID, passports and driving licenses. When finally incinerated for disposal, polycarbonate mainly produces water and carbon dioxide.